The thick film heating circuit is sintered and covered with 5 insulation layers It can directly heat the stainless steel temperature up 150 ℃ / s.Compared with the traditional aluMinum kettle heating plate, the thick film heating element has larger heating area (the thick film heating circuit is evenly covered on the plate), higher power density (60W / cm2), faster temperature response (up to 150 ℃ / s), longer service life (more than 10000 hours) and higher heat transfer efficiency (> 96%).
厚膜加热电路烧结并覆盖5层绝缘层，可直接加热不锈钢温度高达150度/秒。
与传统铝水壶加热板相比，厚膜加热元件具有更大的加热面积（厚膜加热电路均匀地覆盖在板上）、更高的功率密度（60W/cm2), faster temperature response (up to 150 ℃ / s), longer service life (more than 10000 hours) and higher heat transfer efficiency (> 96%).
对于空间有限的电器，厚膜加热器提供高热功率密度和快速加热或冷却响应时间。 被称为“最具影响力的电热元件”，是替代铝制水加热板或浸入式电热元件的理想加热元件。
厚膜釜加热板技术参数
方面 | Φ144mm | 热密度 | >60瓦/平方厘米 |
爬升率 | 150度/秒 | 热效率 | >96% |
加热功率 | 1,800W | 使用寿命 | >10,000 小时 |
额定电压 | 220v | 证书 | CQC、RoHS |
介电强度 | 1,500V/5mA/60秒 | 功率偏差 | -10% - +5% |
漏电流 | 小于或等于0.25mA | 绝缘电阻 | 大于或等于200MΩ |
类型 | PA66+玻璃纤维，耐温≥250度 | 速动恒温器 | 16A，靠近加热管加热回路安装 |
屏蔽热敏电阻 | 正温度系数 | 接地类型 | 点焊 |
连接类型 | 银导体 | 类型 | 厚膜加热 |
厚膜釜加热板的生产工艺：
不锈钢基材的制备
未经涂层的不锈钢基材必须清除污染物（如指纹、灰尘、油污、油脂等），清洁完成后再次接触不锈钢基材时必须戴上手套。
印刷绝缘介质
ESL的绝缘介质通过丝网印刷的方式印刷在相应的不锈钢基板上。 我们建议使用165目无乳胶不锈钢丝网进行印刷，每层烧结厚度应控制在25-30微米之间。 可以使用膜厚测试仪测量绝缘介质的厚度。 三层单独烧结的绝缘介质浆料将达到80微米以上的厚度，以确保足够的绝缘。 请在无尘、洁净的环境下进行印刷和烧结过程，避免因细小杂质而出现小孔，导致击穿电压下降。 浆料在125度干燥，850度烧结（具体烧结曲线请参阅产品说明书）。
印制导体
ESL导体通过丝网印刷的方式印刷在绝缘介质上。 我们建议使用325目20微米乳胶不锈钢丝网进行印刷。 干燥、烧结方法与绝缘介质相同或参照产品说明书。
印刷电阻
ESL 29XXX电阻浆料通过丝网印刷的方式印刷在绝缘介质上。 我们建议使用250目5微米乳胶厚度的不锈钢丝网进行印刷。 一般来说，电阻印刷的宽度为2.4毫米，厚度为21±1微米，螺旋图案为178个方格。 干燥、烧结方法与绝缘介质相同或参照产品说明书。
印刷玻璃保护釉
我们建议使用165目无乳胶不锈钢丝网印刷相应的隔离介质作为保护层。 干燥和烧结的方法如上所述。 电阻器烧结后阻值发生变化是不可避免的，但这不会影响正常使用。
厚膜加热是加热器的新技术，JAYE工业OEM和根据您的具体要求定制，欢迎将您的设计图纸或想法发送给我们。